一般认为,随着HTT 升高,黑碳的碳含量、芳香程度、吸附能力也相应增加

一般认为,随着HTT 升高,黑碳的碳含量、芳香程度、吸附能力也相应增加[51鄄52] ,但是表面积的变化较为
复杂,Pulido鄄Novicio 等[53] 发现,加热生物质产生的焦油会堵塞一部分已经形成的微孔,随着温度升高,焦油挥
发掉,这些微孔得以清空,所以表面积升高之前有一个小的低值。Lua 等[54] 实验表明,热解温度从250 益增
加到500 益,表面积增大,微孔直径增大,但是随着温度进一步升高,黑碳的表面积反而降低[55] ,其原因可能
是高温下相邻微孔的壁被破坏,合并成更大的孔,造成微孔直径增大而表面积下降[56] 。
2. 2

Resultados (inglés) 1:

Generally, with the increase of HTT, black carbon and carbon content, aromatic, adsorption ability increases [51-52], but the surface area of aComplex, Pulido Juan Novicio, [53] found that heating has been a part of biomass tar will plug the micro-holes, as the temperature rises, the tarThese micro-holes can be emptied, so the increased surface area is preceded by a small, low value. Lua [54] experiments show that temperature increased from 250 benefitsAdded to 500 benefit, surface area, pore diameter, but with the temperature increasing, the surface area of the black carbon decreases [55], the reason may beAdjacent is a high temperature porous wall was destroyed, merged into a larger hole, resulting in decreased pore diameter increases with the surface area [56].2.2

Resultados (inglés) 2:

Is generally believed that, as the HTT increases the carbon content of black carbon, aromatic degree of adsorption capacity also increased [51 Juan 52], but the change of surface area is more
complex, Pulido Juan Novicio et al [53] found that heating the biomass produced tar clog pores already formed a part, as the temperature increases, the tar command
sent out, these pores can be empty, so there is a small increase in the surface area of low value before. Lua et al [54] found that the thermal decomposition temperature of from 250 beneficially increases
added 500 gain, increases the surface area, pore diameter increases, but as the temperature is increased further, the surface area of the carbon black may be rather reduced [55], the reason may
be at high temperatures adjacent pore wall is destroyed, merged into a larger hole, resulting in decreased surface area and pore diameter increases [56].
twenty two